EN 1.4869 Casting Alloy vs. AWS ER90S-D2
EN 1.4869 casting alloy belongs to the nickel alloys classification, while AWS ER90S-D2 belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4869 casting alloy and the bottom bar is AWS ER90S-D2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 5.7 | |
| 19 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 260 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1450 |
| Melting Onset (Solidus), °C | 1390 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Conductivity, W/m-K | 10 | |
| 47 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 2.6 |
| Density, g/cm3 | 8.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 1.6 |
| Embodied Energy, MJ/kg | 110 | |
| 21 |
| Embodied Water, L/kg | 300 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 | |
| 980 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 25 |
| Strength to Weight: Bending, points | 17 | |
| 23 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 13 |
| Thermal Shock Resistance, points | 14 | |
| 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.45 to 0.55 | |
| 0.070 to 0.12 |
| Chromium (Cr), % | 24 to 26 | |
| 0 |
| Cobalt (Co), % | 14 to 16 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 11.4 to 23.6 | |
| 95.2 to 97.4 |
| Manganese (Mn), % | 0 to 1.0 | |
| 1.6 to 2.1 |
| Molybdenum (Mo), % | 0 | |
| 0.4 to 0.6 |
| Nickel (Ni), % | 33 to 37 | |
| 0 to 0.15 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 1.0 to 2.0 | |
| 0.5 to 0.8 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |
| Tungsten (W), % | 4.0 to 6.0 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |