EN 1.4876 Stainless Steel vs. S81921 Stainless Steel

Both EN 1.4876 stainless steel and S81921 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4876 stainless steel and the bottom bar is S81921 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
260
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 33
29
Fatigue Strength, MPa 150
370
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Shear Strength, MPa 370
460
Tensile Strength: Ultimate (UTS), MPa 570
710
Tensile Strength: Yield (Proof), MPa 190
500

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 490
430
Maximum Temperature: Mechanical, °C 1100
990
Melting Completion (Liquidus), °C 1400
1430
Melting Onset (Solidus), °C 1350
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 30
14
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.3
2.9
Embodied Energy, MJ/kg 76
41
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 21
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
180
Resilience: Unit (Modulus of Resilience), kJ/m3 94
630
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 3.2
4.0
Thermal Shock Resistance, points 14
20

Alloy Composition

Aluminum (Al), % 0.15 to 0.6
0
Carbon (C), % 0 to 0.12
0 to 0.030
Chromium (Cr), % 19 to 23
19 to 22
Iron (Fe), % 38.6 to 50.7
66.7 to 75.9
Manganese (Mn), % 0 to 2.0
2.0 to 4.0
Molybdenum (Mo), % 0
1.0 to 2.0
Nickel (Ni), % 30 to 34
2.0 to 4.0
Nitrogen (N), % 0
0.14 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0.15 to 0.6
0