EN 1.4886 Stainless Steel vs. ASTM B563 Pd-Ag-Cu

EN 1.4886 stainless steel belongs to the iron alloys classification, while ASTM B563 Pd-Ag-Cu belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is ASTM B563 Pd-Ag-Cu.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 45
7.0 to 17
Poisson's Ratio 0.28
0.37
Shear Modulus, GPa 76
37
Shear Strength, MPa 400
470 to 690
Tensile Strength: Ultimate (UTS), MPa 580
760 to 1170

Thermal Properties

Latent Heat of Fusion, J/g 320
150
Melting Completion (Liquidus), °C 1390
1180
Melting Onset (Solidus), °C 1340
1030
Specific Heat Capacity, J/kg-K 480
260
Thermal Expansion, µm/m-K 15
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
5.6 to 6.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
4.6 to 5.5

Otherwise Unclassified Properties

Density, g/cm3 8.0
11

Common Calculations

Stiffness to Weight: Axial, points 14
5.2
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 20
19 to 30
Strength to Weight: Bending, points 19
17 to 22
Thermal Shock Resistance, points 14
39 to 61

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0
15.5 to 16.5
Iron (Fe), % 38.7 to 49
0
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 33 to 37
0.8 to 1.2
Nitrogen (N), % 0 to 0.1
0
Palladium (Pd), % 0
43 to 45
Phosphorus (P), % 0 to 0.030
0
Platinum (Pt), % 0
0.8 to 1.2
Silicon (Si), % 1.0 to 2.0
0
Silver (Ag), % 0
37 to 39
Sulfur (S), % 0 to 0.015
0
Residuals, % 0
0 to 0.4