EN 1.4886 Stainless Steel vs. AWS E90C-K3

Both EN 1.4886 stainless steel and AWS E90C-K3 are iron alloys. They have 47% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is AWS E90C-K3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
55
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 580
710
Tensile Strength: Yield (Proof), MPa 300
600

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
48
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
3.4
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.7
Embodied Energy, MJ/kg 76
23
Embodied Water, L/kg 190
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
370
Resilience: Unit (Modulus of Resilience), kJ/m3 230
980
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 3.1
13
Thermal Shock Resistance, points 14
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.15
0 to 0.15
Chromium (Cr), % 17 to 20
0 to 0.15
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 38.7 to 49
92.6 to 98.5
Manganese (Mn), % 0 to 2.0
0.75 to 2.3
Molybdenum (Mo), % 0
0.25 to 0.65
Nickel (Ni), % 33 to 37
0.5 to 2.5
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 1.0 to 2.0
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.025
Vanadium (V), % 0
0 to 0.030
Residuals, % 0
0 to 0.5