EN 1.4886 Stainless Steel vs. AWS ERTi-5

EN 1.4886 stainless steel belongs to the iron alloys classification, while AWS ERTi-5 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is AWS ERTi-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 45
10
Fatigue Strength, MPa 280
470
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 76
40
Tensile Strength: Ultimate (UTS), MPa 580
900
Tensile Strength: Yield (Proof), MPa 300
830

Thermal Properties

Latent Heat of Fusion, J/g 320
410
Maximum Temperature: Mechanical, °C 1100
340
Melting Completion (Liquidus), °C 1390
1610
Melting Onset (Solidus), °C 1340
1560
Specific Heat Capacity, J/kg-K 480
560
Thermal Conductivity, W/m-K 12
7.1
Thermal Expansion, µm/m-K 15
9.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
1.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
36
Density, g/cm3 8.0
4.4
Embodied Carbon, kg CO2/kg material 5.4
38
Embodied Energy, MJ/kg 76
610
Embodied Water, L/kg 190
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
87
Resilience: Unit (Modulus of Resilience), kJ/m3 230
3250
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
35
Strength to Weight: Axial, points 20
56
Strength to Weight: Bending, points 19
46
Thermal Diffusivity, mm2/s 3.1
2.9
Thermal Shock Resistance, points 14
63

Alloy Composition

Aluminum (Al), % 0
5.5 to 6.8
Carbon (C), % 0 to 0.15
0 to 0.050
Chromium (Cr), % 17 to 20
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 38.7 to 49
0 to 0.22
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 33 to 37
0
Nitrogen (N), % 0 to 0.1
0 to 0.030
Oxygen (O), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 1.0 to 2.0
0
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
88.2 to 90.9
Vanadium (V), % 0
3.5 to 4.5