EN 1.4886 Stainless Steel vs. Commercially Pure Silver

EN 1.4886 stainless steel belongs to the iron alloys classification, while commercially pure silver belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is commercially pure silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
71
Elongation at Break, % 45
1.1 to 29
Poisson's Ratio 0.28
0.37
Shear Modulus, GPa 76
26
Shear Strength, MPa 400
120 to 190
Tensile Strength: Ultimate (UTS), MPa 580
190 to 340

Thermal Properties

Latent Heat of Fusion, J/g 320
110
Melting Completion (Liquidus), °C 1390
960
Melting Onset (Solidus), °C 1340
960
Specific Heat Capacity, J/kg-K 480
240
Thermal Conductivity, W/m-K 12
420
Thermal Expansion, µm/m-K 15
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
100
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
87

Otherwise Unclassified Properties

Density, g/cm3 8.0
10

Common Calculations

Stiffness to Weight: Axial, points 14
3.8
Stiffness to Weight: Bending, points 24
13
Strength to Weight: Axial, points 20
4.9 to 8.9
Strength to Weight: Bending, points 19
6.9 to 10
Thermal Diffusivity, mm2/s 3.1
170
Thermal Shock Resistance, points 14
9.5 to 17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 17 to 20
0
Iron (Fe), % 38.7 to 49
0
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 33 to 37
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 1.0 to 2.0
0
Silver (Ag), % 0
99.9 to 100
Sulfur (S), % 0 to 0.015
0
Residuals, % 0
0 to 0.1