EN 1.4886 Stainless Steel vs. EN 1.0031 Steel

Both EN 1.4886 stainless steel and EN 1.0031 steel are iron alloys. They have 44% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is EN 1.0031 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
89
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
28
Fatigue Strength, MPa 280
160
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 400
200
Tensile Strength: Ultimate (UTS), MPa 580
310
Tensile Strength: Yield (Proof), MPa 300
210

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1390
1470
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
53
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
1.8
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
1.4
Embodied Energy, MJ/kg 76
18
Embodied Water, L/kg 190
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
78
Resilience: Unit (Modulus of Resilience), kJ/m3 230
120
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
11
Strength to Weight: Bending, points 19
13
Thermal Diffusivity, mm2/s 3.1
14
Thermal Shock Resistance, points 14
9.8

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.1
Chromium (Cr), % 17 to 20
0
Iron (Fe), % 38.7 to 49
98.8 to 100
Manganese (Mn), % 0 to 2.0
0 to 0.7
Nickel (Ni), % 33 to 37
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 1.0 to 2.0
0 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.045