EN 1.4886 Stainless Steel vs. EN 1.0644 Steel

Both EN 1.4886 stainless steel and EN 1.0644 steel are iron alloys. They have 46% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is EN 1.0644 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
17
Fatigue Strength, MPa 280
380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 400
420
Tensile Strength: Ultimate (UTS), MPa 580
690
Tensile Strength: Yield (Proof), MPa 300
570

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
47
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.4
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.8
Embodied Energy, MJ/kg 76
24
Embodied Water, L/kg 190
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
110
Resilience: Unit (Modulus of Resilience), kJ/m3 230
870
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
24
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 3.1
13
Thermal Shock Resistance, points 14
22

Alloy Composition

Aluminum (Al), % 0
0.010 to 0.050
Carbon (C), % 0 to 0.15
0.16 to 0.22
Chromium (Cr), % 17 to 20
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 38.7 to 49
96.1 to 98.4
Manganese (Mn), % 0 to 2.0
1.3 to 1.7
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 33 to 37
0 to 0.4
Niobium (Nb), % 0
0 to 0.070
Nitrogen (N), % 0 to 0.1
0 to 0.020
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 1.0 to 2.0
0.1 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.035
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0.080 to 0.15