EN 1.4886 Stainless Steel vs. S17600 Stainless Steel

Both EN 1.4886 stainless steel and S17600 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is S17600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
270 to 410
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
8.6 to 11
Fatigue Strength, MPa 280
300 to 680
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 400
560 to 880
Tensile Strength: Ultimate (UTS), MPa 580
940 to 1490
Tensile Strength: Yield (Proof), MPa 300
580 to 1310

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 420
550
Maximum Temperature: Mechanical, °C 1100
890
Melting Completion (Liquidus), °C 1390
1430
Melting Onset (Solidus), °C 1340
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 31
13
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
2.9
Embodied Energy, MJ/kg 76
42
Embodied Water, L/kg 190
130

Common Calculations

PREN (Pitting Resistance) 19
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
70 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 230
850 to 4390
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
34 to 54
Strength to Weight: Bending, points 19
28 to 37
Thermal Diffusivity, mm2/s 3.1
4.1
Thermal Shock Resistance, points 14
31 to 50

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0 to 0.15
0 to 0.080
Chromium (Cr), % 17 to 20
16 to 17.5
Iron (Fe), % 38.7 to 49
71.3 to 77.6
Manganese (Mn), % 0 to 2.0
0 to 1.0
Nickel (Ni), % 33 to 37
6.0 to 7.5
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 1.0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0
0.4 to 1.2