EN 1.4886 Stainless Steel vs. S30600 Stainless Steel

Both EN 1.4886 stainless steel and S30600 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is S30600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
45
Fatigue Strength, MPa 280
250
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 400
430
Tensile Strength: Ultimate (UTS), MPa 580
610
Tensile Strength: Yield (Proof), MPa 300
270

Thermal Properties

Latent Heat of Fusion, J/g 320
350
Maximum Temperature: Corrosion, °C 420
410
Maximum Temperature: Mechanical, °C 1100
950
Melting Completion (Liquidus), °C 1390
1380
Melting Onset (Solidus), °C 1340
1330
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 12
14
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
19
Density, g/cm3 8.0
7.6
Embodied Carbon, kg CO2/kg material 5.4
3.6
Embodied Energy, MJ/kg 76
51
Embodied Water, L/kg 190
150

Common Calculations

PREN (Pitting Resistance) 19
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
220
Resilience: Unit (Modulus of Resilience), kJ/m3 230
190
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
22
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 3.1
3.7
Thermal Shock Resistance, points 14
14

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.018
Chromium (Cr), % 17 to 20
17 to 18.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 38.7 to 49
58.9 to 65.3
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 33 to 37
14 to 15.5
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 1.0 to 2.0
3.7 to 4.3
Sulfur (S), % 0 to 0.015
0 to 0.020