EN 1.4886 Stainless Steel vs. S46910 Stainless Steel

Both EN 1.4886 stainless steel and S46910 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is S46910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
270 to 630
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
2.2 to 11
Fatigue Strength, MPa 280
250 to 1020
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 400
410 to 1410
Tensile Strength: Ultimate (UTS), MPa 580
680 to 2470
Tensile Strength: Yield (Proof), MPa 300
450 to 2290

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Maximum Temperature: Corrosion, °C 420
540
Maximum Temperature: Mechanical, °C 1100
810
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 15
11

Otherwise Unclassified Properties

Base Metal Price, % relative 31
18
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
4.1
Embodied Energy, MJ/kg 76
55
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 19
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
48 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 230
510 to 4780
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
24 to 86
Strength to Weight: Bending, points 19
22 to 51
Thermal Shock Resistance, points 14
23 to 84

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.5
Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 17 to 20
11 to 13
Copper (Cu), % 0
1.5 to 3.5
Iron (Fe), % 38.7 to 49
65 to 76
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
3.0 to 5.0
Nickel (Ni), % 33 to 37
8.0 to 10
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 1.0 to 2.0
0 to 0.7
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0
0.5 to 1.2