EN 1.4886 Stainless Steel vs. S82013 Stainless Steel

Both EN 1.4886 stainless steel and S82013 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is S82013 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
260
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
34
Fatigue Strength, MPa 280
400
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Shear Strength, MPa 400
470
Tensile Strength: Ultimate (UTS), MPa 580
710
Tensile Strength: Yield (Proof), MPa 300
500

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 420
430
Maximum Temperature: Mechanical, °C 1100
970
Melting Completion (Liquidus), °C 1390
1420
Melting Onset (Solidus), °C 1340
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 31
11
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.4
2.4
Embodied Energy, MJ/kg 76
34
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 19
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
220
Resilience: Unit (Modulus of Resilience), kJ/m3 230
640
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
26
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 3.1
4.0
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.060
Chromium (Cr), % 17 to 20
19.5 to 22
Copper (Cu), % 0
0.2 to 1.2
Iron (Fe), % 38.7 to 49
70.5 to 77.1
Manganese (Mn), % 0 to 2.0
2.5 to 3.5
Nickel (Ni), % 33 to 37
0.5 to 1.5
Nitrogen (N), % 0 to 0.1
0.2 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 1.0 to 2.0
0 to 0.9
Sulfur (S), % 0 to 0.015
0 to 0.030