EN 1.4938 Stainless Steel vs. ASTM Grade LCC Steel

Both EN 1.4938 stainless steel and ASTM grade LCC steel are iron alloys. They have 84% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4938 stainless steel and the bottom bar is ASTM grade LCC steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 16 to 17
25
Fatigue Strength, MPa 390 to 520
230
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 870 to 1030
570
Tensile Strength: Yield (Proof), MPa 640 to 870
310

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 750
400
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 30
49
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.4
Embodied Energy, MJ/kg 47
18
Embodied Water, L/kg 110
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 160
120
Resilience: Unit (Modulus of Resilience), kJ/m3 1050 to 1920
260
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 31 to 37
20
Strength to Weight: Bending, points 26 to 29
20
Thermal Diffusivity, mm2/s 8.1
13
Thermal Shock Resistance, points 30 to 35
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.080 to 0.15
0 to 0.25
Chromium (Cr), % 11 to 12.5
0
Iron (Fe), % 80.5 to 84.8
96.9 to 100
Manganese (Mn), % 0.4 to 0.9
0 to 1.2
Molybdenum (Mo), % 1.5 to 2.0
0
Nickel (Ni), % 2.0 to 3.0
0
Nitrogen (N), % 0.020 to 0.040
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.045
Vanadium (V), % 0.25 to 0.4
0
Residuals, % 0
0 to 1.0