EN 1.4938 Stainless Steel vs. EN 1.4588 Stainless Steel

Both EN 1.4938 stainless steel and EN 1.4588 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4938 stainless steel and the bottom bar is EN 1.4588 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 16 to 17
34
Fatigue Strength, MPa 390 to 520
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 870 to 1030
540
Tensile Strength: Yield (Proof), MPa 640 to 870
240

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 390
420
Maximum Temperature: Mechanical, °C 750
1100
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 30
15
Thermal Expansion, µm/m-K 11
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 10
33
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.3
6.2
Embodied Energy, MJ/kg 47
84
Embodied Water, L/kg 110
200

Common Calculations

PREN (Pitting Resistance) 18
44
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 160
150
Resilience: Unit (Modulus of Resilience), kJ/m3 1050 to 1920
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 31 to 37
18
Strength to Weight: Bending, points 26 to 29
18
Thermal Diffusivity, mm2/s 8.1
4.0
Thermal Shock Resistance, points 30 to 35
11

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.020
Chromium (Cr), % 11 to 12.5
19 to 21
Copper (Cu), % 0
0.5 to 1.5
Iron (Fe), % 80.5 to 84.8
41.2 to 50.4
Manganese (Mn), % 0.4 to 0.9
0 to 2.0
Molybdenum (Mo), % 1.5 to 2.0
6.0 to 7.0
Nickel (Ni), % 2.0 to 3.0
24 to 26
Nitrogen (N), % 0.020 to 0.040
0.1 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.020
Vanadium (V), % 0.25 to 0.4
0