EN 1.4938 Stainless Steel vs. SAE-AISI O6 Steel

Both EN 1.4938 stainless steel and SAE-AISI O6 steel are iron alloys. They have 84% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4938 stainless steel and the bottom bar is SAE-AISI O6 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
71
Tensile Strength: Ultimate (UTS), MPa 870 to 1030
670 to 2070

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 30
43
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.3
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.3
1.5
Embodied Energy, MJ/kg 47
21
Embodied Water, L/kg 110
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31 to 37
24 to 74
Strength to Weight: Bending, points 26 to 29
22 to 47
Thermal Diffusivity, mm2/s 8.1
12
Thermal Shock Resistance, points 30 to 35
22 to 69

Alloy Composition

Carbon (C), % 0.080 to 0.15
1.3 to 1.6
Chromium (Cr), % 11 to 12.5
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 80.5 to 84.8
94.6 to 97.7
Manganese (Mn), % 0.4 to 0.9
0.3 to 1.1
Molybdenum (Mo), % 1.5 to 2.0
0.2 to 0.3
Nickel (Ni), % 2.0 to 3.0
0 to 0.3
Nitrogen (N), % 0.020 to 0.040
0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.5
0.55 to 1.5
Sulfur (S), % 0 to 0.015
0 to 0.030
Vanadium (V), % 0.25 to 0.4
0

Comparable Variants