EN 1.4938 Stainless Steel vs. Titanium 6-6-2
EN 1.4938 stainless steel belongs to the iron alloys classification, while titanium 6-6-2 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4938 stainless steel and the bottom bar is titanium 6-6-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Elongation at Break, % | 16 to 17 | |
| 6.7 to 9.0 |
| Fatigue Strength, MPa | 390 to 520 | |
| 590 to 670 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 76 | |
| 44 |
| Shear Strength, MPa | 540 to 630 | |
| 670 to 800 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 1030 | |
| 1140 to 1370 |
| Tensile Strength: Yield (Proof), MPa | 640 to 870 | |
| 1040 to 1230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 750 | |
| 310 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1610 |
| Melting Onset (Solidus), °C | 1420 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 540 |
| Thermal Conductivity, W/m-K | 30 | |
| 5.5 |
| Thermal Expansion, µm/m-K | 11 | |
| 9.4 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 1.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 2.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 40 |
| Density, g/cm3 | 7.8 | |
| 4.8 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 29 |
| Embodied Energy, MJ/kg | 47 | |
| 470 |
| Embodied Water, L/kg | 110 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 89 to 99 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 34 |
| Strength to Weight: Axial, points | 31 to 37 | |
| 66 to 79 |
| Strength to Weight: Bending, points | 26 to 29 | |
| 50 to 57 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 2.1 |
| Thermal Shock Resistance, points | 30 to 35 | |
| 75 to 90 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 5.0 to 6.0 |
| Carbon (C), % | 0.080 to 0.15 | |
| 0 to 0.050 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.35 to 1.0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 80.5 to 84.8 | |
| 0.35 to 1.0 |
| Manganese (Mn), % | 0.4 to 0.9 | |
| 0 |
| Molybdenum (Mo), % | 1.5 to 2.0 | |
| 5.0 to 6.0 |
| Nickel (Ni), % | 2.0 to 3.0 | |
| 0 |
| Nitrogen (N), % | 0.020 to 0.040 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.5 to 2.5 |
| Titanium (Ti), % | 0 | |
| 82.8 to 87.8 |
| Vanadium (V), % | 0.25 to 0.4 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |