EN 1.4938 Stainless Steel vs. C36000 Brass
EN 1.4938 stainless steel belongs to the iron alloys classification, while C36000 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4938 stainless steel and the bottom bar is C36000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 100 |
| Elongation at Break, % | 16 to 17 | |
| 5.8 to 23 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 76 | |
| 39 |
| Shear Strength, MPa | 540 to 630 | |
| 210 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 1030 | |
| 330 to 530 |
| Tensile Strength: Yield (Proof), MPa | 640 to 870 | |
| 140 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 750 | |
| 120 |
| Melting Completion (Liquidus), °C | 1460 | |
| 900 |
| Melting Onset (Solidus), °C | 1420 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 30 | |
| 120 |
| Thermal Expansion, µm/m-K | 11 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 23 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 2.6 |
| Embodied Energy, MJ/kg | 47 | |
| 45 |
| Embodied Water, L/kg | 110 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 25 to 62 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1050 to 1920 | |
| 89 to 340 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 31 to 37 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 26 to 29 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 37 |
| Thermal Shock Resistance, points | 30 to 35 | |
| 11 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.080 to 0.15 | |
| 0 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 60 to 63 |
| Iron (Fe), % | 80.5 to 84.8 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 | |
| 2.5 to 3.7 |
| Manganese (Mn), % | 0.4 to 0.9 | |
| 0 |
| Molybdenum (Mo), % | 1.5 to 2.0 | |
| 0 |
| Nickel (Ni), % | 2.0 to 3.0 | |
| 0 |
| Nitrogen (N), % | 0.020 to 0.040 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Vanadium (V), % | 0.25 to 0.4 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 32.5 to 37.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |