EN 1.4951 Stainless Steel vs. AISI 310H Stainless Steel

Both EN 1.4951 stainless steel and AISI 310H stainless steel are iron alloys. Their average alloy composition is basically identical. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4951 stainless steel and the bottom bar is AISI 310H stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
40
Fatigue Strength, MPa 190
200
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 79
79
Shear Strength, MPa 430
400
Tensile Strength: Ultimate (UTS), MPa 630
580
Tensile Strength: Yield (Proof), MPa 220
230

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 450
450
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1410
1410
Melting Onset (Solidus), °C 1360
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
25
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.3
4.3
Embodied Energy, MJ/kg 61
61
Embodied Water, L/kg 190
190

Common Calculations

PREN (Pitting Resistance) 26
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
190
Resilience: Unit (Modulus of Resilience), kJ/m3 130
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 3.9
3.9
Thermal Shock Resistance, points 14
13

Alloy Composition

Carbon (C), % 0.040 to 0.080
0.040 to 0.1
Chromium (Cr), % 24 to 26
24 to 26
Iron (Fe), % 49.1 to 57
49.1 to 57
Manganese (Mn), % 0 to 2.0
0 to 2.0
Nickel (Ni), % 19 to 22
19 to 22
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.7
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030