EN 1.5026 Steel vs. ASTM A182 Grade F122

Both EN 1.5026 steel and ASTM A182 grade F122 are iron alloys. They have 85% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.5026 steel and the bottom bar is ASTM A182 grade F122.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 480
220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
76
Tensile Strength: Ultimate (UTS), MPa 660 to 1980
710

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Maximum Temperature: Mechanical, °C 400
600
Melting Completion (Liquidus), °C 1440
1490
Melting Onset (Solidus), °C 1390
1440
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 47
24
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
10
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
12

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
12
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 1.5
3.0
Embodied Energy, MJ/kg 19
44
Embodied Water, L/kg 46
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24 to 71
25
Strength to Weight: Bending, points 22 to 45
22
Thermal Diffusivity, mm2/s 13
6.4
Thermal Shock Resistance, points 20 to 60
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0 to 0.0050
Carbon (C), % 0.52 to 0.6
0.070 to 0.14
Chromium (Cr), % 0
10 to 11.5
Copper (Cu), % 0
0.3 to 1.7
Iron (Fe), % 96.5 to 97.3
81.3 to 87.7
Manganese (Mn), % 0.6 to 0.9
0 to 0.7
Molybdenum (Mo), % 0
0.25 to 0.6
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0.040 to 0.1
Nitrogen (N), % 0
0.040 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 1.6 to 2.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.5
Vanadium (V), % 0
0.15 to 0.3
Zirconium (Zr), % 0
0 to 0.010