EN 1.5502 Steel vs. AISI 414 Stainless Steel

Both EN 1.5502 steel and AISI 414 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.5502 steel and the bottom bar is AISI 414 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 20
17
Fatigue Strength, MPa 190 to 290
430 to 480
Poisson's Ratio 0.29
0.28
Reduction in Area, % 62 to 76
50
Shear Modulus, GPa 73
76
Shear Strength, MPa 280 to 330
550 to 590
Tensile Strength: Ultimate (UTS), MPa 400 to 1380
900 to 960
Tensile Strength: Yield (Proof), MPa 270 to 440
700 to 790

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
750
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
8.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.1
Embodied Energy, MJ/kg 19
29
Embodied Water, L/kg 47
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 41 to 210
140 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 520
1260 to 1590
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 14 to 49
32 to 34
Strength to Weight: Bending, points 15 to 35
27 to 28
Thermal Diffusivity, mm2/s 14
6.7
Thermal Shock Resistance, points 12 to 40
33 to 35

Alloy Composition

Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.15 to 0.2
0 to 0.15
Chromium (Cr), % 0 to 0.3
11.5 to 13.5
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 98 to 99.249
81.8 to 87.3
Manganese (Mn), % 0.6 to 0.9
0 to 1.0
Nickel (Ni), % 0
1.3 to 2.5
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030

Comparable Variants