EN 1.5510 Steel vs. SAE-AISI 1144 Steel

Both EN 1.5510 steel and SAE-AISI 1144 steel are iron alloys. They have a very high 99% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.5510 steel and the bottom bar is SAE-AISI 1144 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 190
220 to 230
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 21
11 to 17
Fatigue Strength, MPa 220 to 330
280 to 430
Poisson's Ratio 0.29
0.29
Reduction in Area, % 62 to 72
34 to 40
Shear Modulus, GPa 73
72
Shear Strength, MPa 310 to 380
460 to 510
Tensile Strength: Ultimate (UTS), MPa 450 to 1600
750 to 840
Tensile Strength: Yield (Proof), MPa 310 to 520
420 to 690

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 46 to 260
91 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 260 to 710
480 to 1290
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16 to 57
27 to 30
Strength to Weight: Bending, points 17 to 39
23 to 25
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 13 to 47
22 to 24

Alloy Composition

Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.25 to 0.3
0.4 to 0.48
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 97.9 to 99.149
97.5 to 98
Manganese (Mn), % 0.6 to 0.9
1.4 to 1.7
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.3
0
Sulfur (S), % 0 to 0.025
0.24 to 0.33

Comparable Variants