EN 1.5681 Steel vs. EN 1.4826 Stainless Steel

Both EN 1.5681 steel and EN 1.4826 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.5681 steel and the bottom bar is EN 1.4826 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
150
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
9.1
Fatigue Strength, MPa 300
140
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 630
500
Tensile Strength: Yield (Proof), MPa 430
260

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 420
950
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 48
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.9
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 9.0
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 5.0
17
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.9
3.3
Embodied Energy, MJ/kg 25
47
Embodied Water, L/kg 55
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
39
Resilience: Unit (Modulus of Resilience), kJ/m3 490
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
18
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 13
3.7
Thermal Shock Resistance, points 19
11

Alloy Composition

Carbon (C), % 0.060 to 0.12
0.3 to 0.5
Chromium (Cr), % 0
21 to 23
Iron (Fe), % 92.9 to 94.9
60.4 to 68.7
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 4.5 to 5.5
9.0 to 11
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.6
1.0 to 2.5
Sulfur (S), % 0 to 0.020
0 to 0.030