EN 1.7213 Steel vs. EN 1.4565 Stainless Steel

Both EN 1.7213 steel and EN 1.4565 stainless steel are iron alloys. They have 48% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.7213 steel and the bottom bar is EN 1.4565 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
81
Tensile Strength: Ultimate (UTS), MPa 500 to 1550
880

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
12
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
28
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
5.4
Embodied Energy, MJ/kg 20
74
Embodied Water, L/kg 52
210

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 55
31
Strength to Weight: Bending, points 18 to 38
26
Thermal Diffusivity, mm2/s 12
3.2
Thermal Shock Resistance, points 15 to 45
21

Alloy Composition

Carbon (C), % 0.22 to 0.29
0 to 0.030
Chromium (Cr), % 0.9 to 1.2
24 to 26
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 96.7 to 98.1
41.2 to 50.7
Manganese (Mn), % 0.6 to 0.9
5.0 to 7.0
Molybdenum (Mo), % 0.15 to 0.3
4.0 to 5.0
Nickel (Ni), % 0
16 to 19
Niobium (Nb), % 0
0 to 0.15
Nitrogen (N), % 0
0.3 to 0.6
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0.020 to 0.040
0 to 0.015