EN 1.7231 Steel vs. ACI-ASTM CD3MWCuN Steel

Both EN 1.7231 steel and ACI-ASTM CD3MWCuN steel are iron alloys. They have 63% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is ACI-ASTM CD3MWCuN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 12
29
Fatigue Strength, MPa 360 to 500
370
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 790 to 930
790
Tensile Strength: Yield (Proof), MPa 570 to 800
500

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
16
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
4.2
Embodied Energy, MJ/kg 20
58
Embodied Water, L/kg 51
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 100
200
Resilience: Unit (Modulus of Resilience), kJ/m3 870 to 1700
620
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 28 to 33
28
Strength to Weight: Bending, points 24 to 27
24
Thermal Diffusivity, mm2/s 12
4.2
Thermal Shock Resistance, points 23 to 27
22

Alloy Composition

Carbon (C), % 0.38 to 0.45
0 to 0.030
Chromium (Cr), % 0.8 to 1.2
24 to 26
Copper (Cu), % 0
0.5 to 1.0
Iron (Fe), % 96.4 to 98.1
56.6 to 65.3
Manganese (Mn), % 0.6 to 1.0
0 to 1.5
Molybdenum (Mo), % 0.15 to 0.3
3.0 to 4.0
Nickel (Ni), % 0
6.5 to 8.5
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.025
Tungsten (W), % 0
0.5 to 1.0