EN 1.7231 Steel vs. ASTM A732 Cast Steel

Both EN 1.7231 steel and ASTM A732 cast steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is ASTM A732 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 240 to 280
140 to 440
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 12
4.0 to 25
Fatigue Strength, MPa 360 to 500
230 to 750
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72 to 73
Tensile Strength: Ultimate (UTS), MPa 790 to 930
460 to 1470
Tensile Strength: Yield (Proof), MPa 570 to 800
310 to 1340

Thermal Properties

Latent Heat of Fusion, J/g 250
250 to 260
Maximum Temperature: Mechanical, °C 420
400 to 430
Melting Completion (Liquidus), °C 1460
1440 to 1460
Melting Onset (Solidus), °C 1420
1400 to 1420
Specific Heat Capacity, J/kg-K 470
470 to 480
Thermal Conductivity, W/m-K 46
39 to 50
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.1 to 7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.2 to 8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
2.0 to 3.8
Density, g/cm3 7.8
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 1.5
1.4 to 1.7
Embodied Energy, MJ/kg 20
19 to 24
Embodied Water, L/kg 51
47 to 54

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 100
45 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 870 to 1700
260 to 4770
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 28 to 33
16 to 52
Strength to Weight: Bending, points 24 to 27
17 to 37
Thermal Diffusivity, mm2/s 12
10 to 14
Thermal Shock Resistance, points 23 to 27
14 to 43