EN 1.7231 Steel vs. Nickel Beryllium 360

EN 1.7231 steel belongs to the iron alloys classification, while nickel beryllium 360 belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is nickel beryllium 360.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 12
1.0 to 30
Fatigue Strength, MPa 360 to 500
260 to 710
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 790 to 930
780 to 1860
Tensile Strength: Yield (Proof), MPa 570 to 800
380 to 1590

Thermal Properties

Melting Completion (Liquidus), °C 1460
1330
Melting Onset (Solidus), °C 1420
1200
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 46
48
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
5.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
5.4

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.3

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 100
12 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 870 to 1700
360 to 3440
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 28 to 33
26 to 62
Strength to Weight: Bending, points 24 to 27
23 to 41
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 23 to 27
19 to 46

Comparable Variants