EN 1.7231 steel belongs to the iron alloys classification, while C24000 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is C24000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
42
Tensile Strength: Ultimate (UTS), MPa 790 to 930
310 to 640

Thermal Properties

Latent Heat of Fusion, J/g 250
190
Maximum Temperature: Mechanical, °C 420
160
Melting Completion (Liquidus), °C 1460
1000
Melting Onset (Solidus), °C 1420
970
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 46
140
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
32
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
34

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
27
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.5
2.6
Embodied Energy, MJ/kg 20
43
Embodied Water, L/kg 51
320

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 28 to 33
10 to 21
Strength to Weight: Bending, points 24 to 27
12 to 20
Thermal Diffusivity, mm2/s 12
43
Thermal Shock Resistance, points 23 to 27
10 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.38 to 0.45
0
Chromium (Cr), % 0.8 to 1.2
0
Copper (Cu), % 0
78.5 to 81.5
Iron (Fe), % 96.4 to 98.1
0 to 0.050
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0.6 to 1.0
0
Molybdenum (Mo), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.6
0
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
18.2 to 21.5
Residuals, % 0
0 to 0.2