EN 1.7231 Steel vs. C44300 Brass

EN 1.7231 steel belongs to the iron alloys classification, while C44300 brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is C44300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
41
Tensile Strength: Ultimate (UTS), MPa 790 to 930
350
Tensile Strength: Yield (Proof), MPa 570 to 800
120

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Maximum Temperature: Mechanical, °C 420
140
Melting Completion (Liquidus), °C 1460
940
Melting Onset (Solidus), °C 1420
900
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 46
110
Thermal Expansion, µm/m-K 13
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
25
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
27

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
26
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 1.5
2.8
Embodied Energy, MJ/kg 20
46
Embodied Water, L/kg 51
330

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 870 to 1700
65
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 28 to 33
12
Strength to Weight: Bending, points 24 to 27
13
Thermal Diffusivity, mm2/s 12
35
Thermal Shock Resistance, points 23 to 27
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Arsenic (As), % 0
0.020 to 0.060
Carbon (C), % 0.38 to 0.45
0
Chromium (Cr), % 0.8 to 1.2
0
Copper (Cu), % 0
70 to 73
Iron (Fe), % 96.4 to 98.1
0 to 0.060
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0.6 to 1.0
0
Molybdenum (Mo), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.6
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0.9 to 1.2
Zinc (Zn), % 0
25.2 to 29.1
Residuals, % 0
0 to 0.4