EN 1.7231 Steel vs. N06603 Nickel

EN 1.7231 steel belongs to the iron alloys classification, while N06603 nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is N06603 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 12
28
Fatigue Strength, MPa 360 to 500
230
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 790 to 930
740
Tensile Strength: Yield (Proof), MPa 570 to 800
340

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 420
1000
Melting Completion (Liquidus), °C 1460
1340
Melting Onset (Solidus), °C 1420
1300
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 46
11
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
50
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.5
8.4
Embodied Energy, MJ/kg 20
120
Embodied Water, L/kg 51
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 100
170
Resilience: Unit (Modulus of Resilience), kJ/m3 870 to 1700
300
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 28 to 33
25
Strength to Weight: Bending, points 24 to 27
22
Thermal Diffusivity, mm2/s 12
2.9
Thermal Shock Resistance, points 23 to 27
20

Alloy Composition

Aluminum (Al), % 0
2.4 to 3.0
Carbon (C), % 0.38 to 0.45
0.2 to 0.4
Chromium (Cr), % 0.8 to 1.2
24 to 26
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 96.4 to 98.1
8.0 to 11
Manganese (Mn), % 0.6 to 1.0
0 to 0.15
Molybdenum (Mo), % 0.15 to 0.3
0
Nickel (Ni), % 0
57.7 to 65.6
Phosphorus (P), % 0 to 0.025
0 to 0.2
Silicon (Si), % 0 to 0.6
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0.010 to 0.25
Yttrium (Y), % 0
0.010 to 0.15
Zinc (Zn), % 0
0.010 to 0.1