EN 1.7231 Steel vs. N07750 Nickel

EN 1.7231 steel belongs to the iron alloys classification, while N07750 nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is N07750 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 12
25
Fatigue Strength, MPa 360 to 500
520
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 790 to 930
1200
Tensile Strength: Yield (Proof), MPa 570 to 800
820

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 420
960
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 46
13
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
60
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.5
10
Embodied Energy, MJ/kg 20
150
Embodied Water, L/kg 51
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 100
270
Resilience: Unit (Modulus of Resilience), kJ/m3 870 to 1700
1770
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 28 to 33
40
Strength to Weight: Bending, points 24 to 27
30
Thermal Diffusivity, mm2/s 12
3.3
Thermal Shock Resistance, points 23 to 27
36

Alloy Composition

Aluminum (Al), % 0
0.4 to 1.0
Carbon (C), % 0.38 to 0.45
0 to 0.080
Chromium (Cr), % 0.8 to 1.2
14 to 17
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 96.4 to 98.1
5.0 to 9.0
Manganese (Mn), % 0.6 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.15 to 0.3
0
Nickel (Ni), % 0
70 to 77.7
Niobium (Nb), % 0
0.7 to 1.2
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.6
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
2.3 to 2.8