EN 1.7323 Steel vs. AWS E409Nb

Both EN 1.7323 steel and AWS E409Nb are iron alloys. They have 86% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7323 steel and the bottom bar is AWS E409Nb.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 480 to 1460
500

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 45
25
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
13
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
2.9
Embodied Energy, MJ/kg 20
42
Embodied Water, L/kg 50
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17 to 52
18
Strength to Weight: Bending, points 17 to 36
18
Thermal Diffusivity, mm2/s 12
6.8
Thermal Shock Resistance, points 14 to 43
14

Alloy Composition

Carbon (C), % 0.17 to 0.23
0 to 0.12
Chromium (Cr), % 0.3 to 0.6
11 to 14
Copper (Cu), % 0 to 0.25
0 to 0.75
Iron (Fe), % 97.1 to 98.4
80.2 to 88.5
Manganese (Mn), % 0.7 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.4 to 0.5
0 to 0.75
Nickel (Ni), % 0
0 to 0.6
Niobium (Nb), % 0
0.5 to 1.5
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0.020 to 0.040
0 to 0.030