EN 1.7380 steel belongs to the iron alloys classification, while AWS BAg-2 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is EN 1.7380 steel and the bottom bar is AWS BAg-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
82
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 74
31
Tensile Strength: Ultimate (UTS), MPa 540 to 550
180

Thermal Properties

Latent Heat of Fusion, J/g 260
130
Melting Completion (Liquidus), °C 1470
700
Melting Onset (Solidus), °C 1430
610
Specific Heat Capacity, J/kg-K 470
310
Thermal Expansion, µm/m-K 13
22

Otherwise Unclassified Properties

Density, g/cm3 7.9
8.9
Embodied Carbon, kg CO2/kg material 1.8
35
Embodied Energy, MJ/kg 23
550

Common Calculations

Stiffness to Weight: Axial, points 13
5.1
Stiffness to Weight: Bending, points 24
16
Strength to Weight: Axial, points 19 to 20
5.6
Strength to Weight: Bending, points 19
7.9
Thermal Shock Resistance, points 15 to 16
7.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0
17 to 19
Carbon (C), % 0.080 to 0.14
0
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0 to 0.3
25 to 27
Iron (Fe), % 94.6 to 96.6
0
Manganese (Mn), % 0.4 to 0.8
0
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
34 to 36
Sulfur (S), % 0 to 0.010
0
Zinc (Zn), % 0
19 to 23
Residuals, % 0
0 to 0.15