AWS BAg-2 (P07350) Filler Metal

AWS BAg-2 is a silver-based filler metal for brazing. Cited properties are appropriate for the as-fabricated (no temper or treatment) condition. BAg-2 is the AWS designation for this material. P07350 is the UNS number.

It has a moderately high tensile strength among silver-based braze fillers. In addition, it has a fairly low melting temperature and a moderately low density.

The graph bars on the material properties cards below compare AWS BAg-2 to: silver-based braze fillers (top), all alloys in the same category (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

82 GPa 12 x 106 psi

Poisson's Ratio


Shear Modulus

31 GPa 4.5 x 106 psi

Tensile Strength: Ultimate (UTS)

180 MPa 26 x 103 psi

Thermal Properties

Brazing Temperature

700 to 840 °C 1300 to 1550 °F

Latent Heat of Fusion

130 J/g

Melting Completion (Liquidus)

700 °C 1300 °F

Melting Onset (Solidus)

610 °C 1120 °F

Specific Heat Capacity

310 J/kg-K 0.073 BTU/lb-°F

Thermal Expansion

22 µm/m-K

Otherwise Unclassified Properties


8.9 g/cm3 560 lb/ft3

Embodied Carbon

35 kg CO2/kg material

Embodied Energy

550 MJ/kg 230 x 103 BTU/lb

Common Calculations

Stiffness to Weight: Axial

5.1 points

Stiffness to Weight: Bending

16 points

Strength to Weight: Axial

5.6 points

Strength to Weight: Bending

7.9 points

Thermal Shock Resistance

7.0 points

Alloy Composition

Silver (Ag)Ag 34 to 36
Copper (Cu)Cu 25 to 27
Zinc (Zn)Zn 19 to 23
Cadmium (Cd)Cd 17 to 19
Residualsres. 0 to 0.15

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

AWS A5.8: Specification for Filler Metals for Brazing and Braze Welding