AWS BAg-2a (P07300) Filler Metal

AWS BAg-2a is a silver-based filler metal for brazing. Cited properties are appropriate for the as-fabricated (no temper or treatment) condition. BAg-2a is the AWS designation for this material. P07300 is the UNS number.

It has a fairly low melting temperature and a moderately low density among silver-based braze fillers.

The graph bars on the material properties cards below compare AWS BAg-2a to: silver-based braze fillers (top), all alloys in the same category (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

83 GPa 12 x 106 psi

Poisson's Ratio


Shear Modulus

31 GPa 4.5 x 106 psi

Tensile Strength: Ultimate (UTS)

170 MPa 25 x 103 psi

Thermal Properties

Brazing Temperature

690 to 840 °C 1270 to 1550 °F

Latent Heat of Fusion

130 J/g

Melting Completion (Liquidus)

710 °C 1310 °F

Melting Onset (Solidus)

610 °C 1120 °F

Specific Heat Capacity

310 J/kg-K 0.074 BTU/lb-°F

Thermal Expansion

23 µm/m-K

Otherwise Unclassified Properties


8.8 g/cm3 550 lb/ft3

Embodied Carbon

30 kg CO2/kg material

Embodied Energy

470 MJ/kg 200 x 103 BTU/lb

Common Calculations

Stiffness to Weight: Axial

5.2 points

Stiffness to Weight: Bending

17 points

Strength to Weight: Axial

5.4 points

Strength to Weight: Bending

7.8 points

Thermal Shock Resistance

6.5 points

Alloy Composition

Silver (Ag)Ag 29 to 31
Copper (Cu)Cu 26 to 28
Zinc (Zn)Zn 21 to 25
Cadmium (Cd)Cd 19 to 21
Residualsres. 0 to 0.15

All values are % weight. Ranges represent what is permitted under applicable standards.