AWS BAg-27 (P07251) Filler Metal

AWS BAg-27 is a silver-based filler metal for brazing. Cited properties are appropriate for the as-fabricated (no temper or treatment) condition. BAg-27 is the AWS designation for this material. P07251 is the UNS number.

It has a fairly low melting temperature among silver-based braze fillers. In addition, it has a fairly high heat capacity and a fairly low density.

The graph bars on the material properties cards below compare AWS BAg-27 to: silver-based braze fillers (top), all alloys in the same category (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

88 GPa 13 x 106 psi

Poisson's Ratio


Shear Modulus

33 GPa 4.8 x 106 psi

Tensile Strength: Ultimate (UTS)

160 MPa 23 x 103 psi

Thermal Properties

Brazing Temperature

710 to 860 °C 1310 to 1580 °F

Latent Heat of Fusion

140 J/g

Melting Completion (Liquidus)

750 °C 1370 °F

Melting Onset (Solidus)

610 °C 1120 °F

Specific Heat Capacity

330 J/kg-K 0.078 BTU/lb-°F

Thermal Expansion

22 µm/m-K

Otherwise Unclassified Properties


8.7 g/cm3 540 lb/ft3

Embodied Carbon

25 kg CO2/kg material

Embodied Energy

400 MJ/kg 170 x 103 BTU/lb

Common Calculations

Stiffness to Weight: Axial

5.7 points

Stiffness to Weight: Bending

17 points

Strength to Weight: Axial

5.1 points

Strength to Weight: Bending

7.6 points

Thermal Shock Resistance

5.9 points

Alloy Composition

Copper (Cu)Cu 34 to 36
Zinc (Zn)Zn 24.5 to 28.5
Silver (Ag)Ag 24 to 26
Cadmium (Cd)Cd 12.5 to 14.5
Residualsres. 0 to 0.15

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

AWS A5.8: Specification for Filler Metals for Brazing and Braze Welding