MakeItFrom.com
Menu (ESC)

EN 1.8159 Steel vs. AWS E308LMo

Both EN 1.8159 steel and AWS E308LMo are iron alloys. They have 67% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.8159 steel and the bottom bar is AWS E308LMo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 660 to 1980
580

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
16
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.9
3.8
Embodied Energy, MJ/kg 26
53
Embodied Water, L/kg 52
160

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23 to 70
21
Strength to Weight: Bending, points 21 to 45
20
Thermal Diffusivity, mm2/s 13
4.2
Thermal Shock Resistance, points 19 to 58
15

Alloy Composition

Carbon (C), % 0.47 to 0.55
0 to 0.040
Chromium (Cr), % 0.9 to 1.2
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 96.4 to 97.8
59.6 to 70.5
Manganese (Mn), % 0.7 to 1.1
0.5 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0
9.0 to 12
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.030
Vanadium (V), % 0.1 to 0.25
0