EN 1.8818 Steel vs. AWS E410NiMo

Both EN 1.8818 steel and AWS E410NiMo are iron alloys. They have 83% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.8818 steel and the bottom bar is AWS E410NiMo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
17
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 440
850

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
24
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
10
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
2.4
Embodied Energy, MJ/kg 21
34
Embodied Water, L/kg 49
110

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
30
Strength to Weight: Bending, points 16
26
Thermal Diffusivity, mm2/s 13
6.5
Thermal Shock Resistance, points 13
23

Alloy Composition

Aluminum (Al), % 0.015 to 0.034
0
Carbon (C), % 0 to 0.15
0 to 0.060
Chromium (Cr), % 0 to 0.35
11 to 12.5
Copper (Cu), % 0 to 0.6
0 to 0.75
Iron (Fe), % 95.9 to 99.985
79 to 84.6
Manganese (Mn), % 0 to 1.6
0 to 1.0
Molybdenum (Mo), % 0 to 0.13
0.4 to 0.7
Nickel (Ni), % 0 to 0.35
4.0 to 5.0
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.017
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.55
0 to 0.9
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0 to 0.060
0
Vanadium (V), % 0 to 0.1
0