Both EN 1.8838 steel and K93600 alloy are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.8838 steel and the bottom bar is K93600 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
140
Elongation at Break, % 19
5.0 to 35
Shear Strength, MPa 380
320 to 380
Tensile Strength: Ultimate (UTS), MPa 610
480 to 810
Tensile Strength: Yield (Proof), MPa 430
280 to 750

Thermal Properties

Maximum Temperature: Mechanical, °C 410
440
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
520
Thermal Conductivity, W/m-K 44
13
Thermal Expansion, µm/m-K 13
7.3

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
2.4

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.1

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
21 to 280
Resilience: Unit (Modulus of Resilience), kJ/m3 500
280 to 2050
Stiffness to Weight: Axial, points 13
9.4
Stiffness to Weight: Bending, points 24
21
Strength to Weight: Axial, points 21
16 to 28
Strength to Weight: Bending, points 20
17 to 24
Thermal Diffusivity, mm2/s 12
3.1
Thermal Shock Resistance, points 18
34 to 57