EN 1.8881 Steel vs. ASTM Grade HE Steel

Both EN 1.8881 steel and ASTM grade HE steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.8881 steel and the bottom bar is ASTM grade HE steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16
10
Fatigue Strength, MPa 460
160
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 830
670
Tensile Strength: Yield (Proof), MPa 710
310

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 40
14
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
19
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.9
3.5
Embodied Energy, MJ/kg 26
50
Embodied Water, L/kg 54
190

Common Calculations

PREN (Pitting Resistance) 2.0
29
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
56
Resilience: Unit (Modulus of Resilience), kJ/m3 1320
240
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 29
24
Strength to Weight: Bending, points 25
22
Thermal Diffusivity, mm2/s 11
3.6
Thermal Shock Resistance, points 24
14

Alloy Composition

Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.2
0.2 to 0.5
Chromium (Cr), % 0 to 1.5
26 to 30
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 91.9 to 100
53.9 to 65.8
Manganese (Mn), % 0 to 1.7
0 to 2.0
Molybdenum (Mo), % 0 to 0.7
0 to 0.5
Nickel (Ni), % 0 to 2.5
8.0 to 11
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.8
0 to 2.0
Sulfur (S), % 0 to 0.0080
0 to 0.040
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0 to 0.12
0
Zirconium (Zr), % 0 to 0.15
0