EN 1.8935 Steel vs. ASTM A36 Carbon Steel

Both EN 1.8935 steel and ASTM A36 carbon steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.8935 steel and the bottom bar is ASTM A36 carbon steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
22
Fatigue Strength, MPa 330
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 400
300
Tensile Strength: Ultimate (UTS), MPa 640
480
Tensile Strength: Yield (Proof), MPa 490
290

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
50
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
12
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
14

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 24
18
Embodied Water, L/kg 51
44

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
92
Resilience: Unit (Modulus of Resilience), kJ/m3 640
220
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 19
16

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
0
Carbon (C), % 0 to 0.2
0 to 0.26
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 95.2 to 98.9
99.25 to 100
Manganese (Mn), % 1.1 to 1.7
0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.8
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.025
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.6
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.050
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.2
0