EN 1.8935 Steel vs. EN 1.3956 Stainless Steel

Both EN 1.8935 steel and EN 1.3956 stainless steel are iron alloys. They have 59% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.8935 steel and the bottom bar is EN 1.3956 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
27
Fatigue Strength, MPa 330
240
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 640
650
Tensile Strength: Yield (Proof), MPa 490
330

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1080
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
22
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
4.8
Embodied Energy, MJ/kg 24
68
Embodied Water, L/kg 51
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
150
Resilience: Unit (Modulus of Resilience), kJ/m3 640
270
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
23
Strength to Weight: Bending, points 21
21
Thermal Shock Resistance, points 19
18

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
0
Carbon (C), % 0 to 0.2
0 to 0.060
Chromium (Cr), % 0 to 0.3
20.5 to 23.5
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 95.2 to 98.9
51.9 to 62.1
Manganese (Mn), % 1.1 to 1.7
4.0 to 6.0
Molybdenum (Mo), % 0 to 0.1
1.5 to 3.0
Nickel (Ni), % 0 to 0.8
11.5 to 13.5
Niobium (Nb), % 0 to 0.050
0.1 to 0.3
Nitrogen (N), % 0 to 0.025
0.2 to 0.4
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.2
0.1 to 0.3