EN 1.8935 Steel vs. EN 1.8828 Steel

Both EN 1.8935 steel and EN 1.8828 steel are iron alloys. They have a very high 99% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.8935 steel and the bottom bar is EN 1.8828 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
22
Fatigue Strength, MPa 330
310
Impact Strength: V-Notched Charpy, J 71
110
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 400
370
Tensile Strength: Ultimate (UTS), MPa 640
580
Tensile Strength: Yield (Proof), MPa 490
440

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.6
Embodied Energy, MJ/kg 24
21
Embodied Water, L/kg 51
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 640
530
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 19
17

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
0.020 to 0.040
Carbon (C), % 0 to 0.2
0 to 0.16
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 95.2 to 98.9
96.7 to 99.98
Manganese (Mn), % 1.1 to 1.7
0 to 1.7
Molybdenum (Mo), % 0 to 0.1
0 to 0.2
Nickel (Ni), % 0 to 0.8
0 to 0.5
Niobium (Nb), % 0 to 0.050
0 to 0.050
Nitrogen (N), % 0 to 0.025
0 to 0.020
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.6
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.0050
Titanium (Ti), % 0 to 0.030
0 to 0.050
Vanadium (V), % 0 to 0.2
0 to 0.1