EN 2.4680 Cast Nickel vs. EN 1.0314 Steel
EN 2.4680 cast nickel belongs to the nickel alloys classification, while EN 1.0314 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 2.4680 cast nickel and the bottom bar is EN 1.0314 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 9.1 | |
| 24 to 25 |
| Fatigue Strength, MPa | 120 | |
| 140 to 220 |
| Poisson's Ratio | 0.26 | |
| 0.29 |
| Shear Modulus, GPa | 84 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 600 | |
| 320 to 400 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 190 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1050 | |
| 400 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1470 |
| Melting Onset (Solidus), °C | 1320 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 14 | |
| 53 |
| Thermal Expansion, µm/m-K | 15 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 1.8 |
| Density, g/cm3 | 8.0 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 9.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 130 | |
| 18 |
| Embodied Water, L/kg | 350 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 45 | |
| 68 to 87 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 | |
| 95 to 250 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 21 | |
| 11 to 14 |
| Strength to Weight: Bending, points | 20 | |
| 13 to 15 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 14 |
| Thermal Shock Resistance, points | 14 | |
| 10 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.030 |
| Chromium (Cr), % | 48 to 52 | |
| 0 |
| Iron (Fe), % | 0 to 1.0 | |
| 99.365 to 99.78 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.2 to 0.4 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 42.9 to 51 | |
| 0 |
| Niobium (Nb), % | 1.0 to 1.8 | |
| 0 |
| Nitrogen (N), % | 0 to 0.16 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.025 |