EN 2.4964 Cobalt vs. EN 1.8838 Steel

EN 2.4964 cobalt belongs to the cobalt alloys classification, while EN 1.8838 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 2.4964 cobalt and the bottom bar is EN 1.8838 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 40
19
Fatigue Strength, MPa 220
290
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 960
610
Tensile Strength: Yield (Proof), MPa 390
430

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Melting Completion (Liquidus), °C 1630
1460
Melting Onset (Solidus), °C 1550
1420
Specific Heat Capacity, J/kg-K 400
470
Thermal Conductivity, W/m-K 15
44
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
8.7

Otherwise Unclassified Properties

Density, g/cm3 9.6
7.8
Embodied Carbon, kg CO2/kg material 9.8
1.7
Embodied Energy, MJ/kg 140
23
Embodied Water, L/kg 450
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 310
100
Resilience: Unit (Modulus of Resilience), kJ/m3 340
500
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 28
21
Strength to Weight: Bending, points 23
20
Thermal Diffusivity, mm2/s 3.9
12
Thermal Shock Resistance, points 25
18

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.054
Carbon (C), % 0.050 to 0.15
0 to 0.18
Chromium (Cr), % 19 to 21
0 to 0.35
Cobalt (Co), % 46.4 to 58
0
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 0 to 3.0
95 to 99.985
Manganese (Mn), % 0 to 2.0
0 to 1.8
Molybdenum (Mo), % 0
0 to 0.23
Nickel (Ni), % 9.0 to 11
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.027
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.65
Sulfur (S), % 0 to 0.015
0 to 0.025
Titanium (Ti), % 0
0 to 0.060
Tungsten (W), % 14 to 16
0
Vanadium (V), % 0
0 to 0.14