EN AC-45000 Aluminum vs. 333.0 Aluminum
Both EN AC-45000 aluminum and 333.0 aluminum are aluminum alloys. They have a very high 97% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN AC-45000 aluminum and the bottom bar is 333.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 77 | |
| 90 to 110 |
| Elastic (Young's, Tensile) Modulus, GPa | 73 | |
| 73 |
| Elongation at Break, % | 1.1 | |
| 1.0 to 2.0 |
| Fatigue Strength, MPa | 75 | |
| 83 to 100 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 28 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 110 | |
| 130 to 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 470 | |
| 520 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 590 |
| Melting Onset (Solidus), °C | 520 | |
| 530 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 880 |
| Thermal Conductivity, W/m-K | 120 | |
| 100 to 140 |
| Thermal Expansion, µm/m-K | 22 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 26 to 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 81 | |
| 83 to 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 10 |
| Density, g/cm3 | 3.0 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 7.6 |
| Embodied Energy, MJ/kg | 140 | |
| 140 |
| Embodied Water, L/kg | 1070 | |
| 1040 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.7 | |
| 2.1 to 4.6 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 80 | |
| 120 to 290 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 47 | |
| 49 |
| Strength to Weight: Axial, points | 17 | |
| 22 to 27 |
| Strength to Weight: Bending, points | 24 | |
| 29 to 34 |
| Thermal Diffusivity, mm2/s | 47 | |
| 42 to 57 |
| Thermal Shock Resistance, points | 8.0 | |
| 11 to 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 82.2 to 91.8 | |
| 81.8 to 89 |
| Chromium (Cr), % | 0 to 0.15 | |
| 0 |
| Copper (Cu), % | 3.0 to 5.0 | |
| 3.0 to 4.0 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 1.0 |
| Lead (Pb), % | 0 to 0.3 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.55 | |
| 0.050 to 0.5 |
| Manganese (Mn), % | 0.2 to 0.65 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.45 | |
| 0 to 0.5 |
| Silicon (Si), % | 5.0 to 7.0 | |
| 8.0 to 10 |
| Tin (Sn), % | 0 to 0.15 | |
| 0 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Residuals, % | 0 to 0.35 | |
| 0 to 0.5 |