EN AC-48100 Aluminum vs. 2014 Aluminum

Both EN AC-48100 aluminum and 2014 aluminum are aluminum alloys. They have 83% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN AC-48100 aluminum and the bottom bar is 2014 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 76
72
Elongation at Break, % 1.1
1.5 to 16
Fatigue Strength, MPa 120 to 130
90 to 160
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 29
27
Tensile Strength: Ultimate (UTS), MPa 240 to 330
190 to 500
Tensile Strength: Yield (Proof), MPa 190 to 300
100 to 440

Thermal Properties

Latent Heat of Fusion, J/g 640
400
Maximum Temperature: Mechanical, °C 170
210
Melting Completion (Liquidus), °C 580
630
Melting Onset (Solidus), °C 470
510
Specific Heat Capacity, J/kg-K 880
870
Thermal Conductivity, W/m-K 130
150
Thermal Expansion, µm/m-K 20
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
40
Electrical Conductivity: Equal Weight (Specific), % IACS 87
120

Otherwise Unclassified Properties

Base Metal Price, % relative 11
11
Density, g/cm3 2.8
3.0
Embodied Carbon, kg CO2/kg material 7.3
8.1
Embodied Energy, MJ/kg 130
150
Embodied Water, L/kg 940
1130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.3 to 3.6
6.6 to 56
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 580
76 to 1330
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 51
46
Strength to Weight: Axial, points 24 to 33
18 to 46
Strength to Weight: Bending, points 31 to 38
25 to 46
Thermal Diffusivity, mm2/s 55
58
Thermal Shock Resistance, points 11 to 16
8.4 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 72.1 to 79.8
90.4 to 95
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 4.0 to 5.0
3.9 to 5.0
Iron (Fe), % 0 to 1.3
0 to 0.7
Magnesium (Mg), % 0.25 to 0.65
0.2 to 0.8
Manganese (Mn), % 0 to 0.5
0.4 to 1.2
Nickel (Ni), % 0 to 0.3
0
Silicon (Si), % 16 to 18
0.5 to 1.2
Tin (Sn), % 0 to 0.15
0
Titanium (Ti), % 0 to 0.25
0 to 0.15
Zinc (Zn), % 0 to 1.5
0 to 0.25
Zirconium (Zr), % 0
0 to 0.2
Residuals, % 0 to 0.25
0 to 0.15