CC333G bronze belongs to the copper alloys classification, while EN 1.4325 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is EN 1.4325 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
180
Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 13
45
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 45
77
Tensile Strength: Ultimate (UTS), MPa 710
650
Tensile Strength: Yield (Proof), MPa 310
210

Thermal Properties

Latent Heat of Fusion, J/g 230
290
Maximum Temperature: Mechanical, °C 230
930
Melting Completion (Liquidus), °C 1080
1430
Melting Onset (Solidus), °C 1020
1380
Specific Heat Capacity, J/kg-K 440
480
Thermal Conductivity, W/m-K 38
16
Thermal Expansion, µm/m-K 18
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 29
15
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 3.5
3.0
Embodied Energy, MJ/kg 56
42
Embodied Water, L/kg 380
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
230
Resilience: Unit (Modulus of Resilience), kJ/m3 410
110
Stiffness to Weight: Axial, points 8.0
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 24
23
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 10
4.3
Thermal Shock Resistance, points 24
15

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Carbon (C), % 0
0.030 to 0.15
Chromium (Cr), % 0 to 0.050
17 to 19
Copper (Cu), % 76 to 83
0
Iron (Fe), % 3.0 to 5.5
67.8 to 75
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0 to 2.0
Nickel (Ni), % 3.7 to 6.0
8.0 to 10
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0