CC333G Bronze vs. C12600 Copper

Both CC333G bronze and C12600 copper are copper alloys. They have 80% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is CC333G bronze and the bottom bar is C12600 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 13
56
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 45
56
Tensile Strength: Ultimate (UTS), MPa 710
270
Tensile Strength: Yield (Proof), MPa 310
69

Thermal Properties

Latent Heat of Fusion, J/g 230
210
Maximum Temperature: Mechanical, °C 230
200
Melting Completion (Liquidus), °C 1080
1080
Melting Onset (Solidus), °C 1020
1030
Specific Heat Capacity, J/kg-K 440
390
Thermal Conductivity, W/m-K 38
130
Thermal Expansion, µm/m-K 18
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
29
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
29

Otherwise Unclassified Properties

Base Metal Price, % relative 29
30
Density, g/cm3 8.3
8.9
Embodied Carbon, kg CO2/kg material 3.5
2.6
Embodied Energy, MJ/kg 56
41
Embodied Water, L/kg 380
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
110
Resilience: Unit (Modulus of Resilience), kJ/m3 410
21
Stiffness to Weight: Axial, points 8.0
7.2
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 24
8.2
Strength to Weight: Bending, points 21
10
Thermal Diffusivity, mm2/s 10
39
Thermal Shock Resistance, points 24
9.5

Alloy Composition

Aluminum (Al), % 8.5 to 10.5
0
Bismuth (Bi), % 0 to 0.010
0
Chromium (Cr), % 0 to 0.050
0
Copper (Cu), % 76 to 83
99.5 to 99.8
Iron (Fe), % 3.0 to 5.5
0
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 3.0
0
Nickel (Ni), % 3.7 to 6.0
0
Phosphorus (P), % 0
0.2 to 0.4
Silicon (Si), % 0 to 0.1
0
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.5
0