CR022A Copper vs. ASTM A182 Grade F3VCb

CR022A copper belongs to the copper alloys classification, while ASTM A182 grade F3VCb belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CR022A copper and the bottom bar is ASTM A182 grade F3VCb.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 15
21
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
74
Tensile Strength: Ultimate (UTS), MPa 230
670
Tensile Strength: Yield (Proof), MPa 140
460

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Maximum Temperature: Mechanical, °C 200
470
Melting Completion (Liquidus), °C 1090
1470
Melting Onset (Solidus), °C 1040
1430
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 380
40
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 100
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 31
4.5
Density, g/cm3 9.0
7.9
Embodied Carbon, kg CO2/kg material 2.6
2.4
Embodied Energy, MJ/kg 41
33
Embodied Water, L/kg 310
64

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
120
Resilience: Unit (Modulus of Resilience), kJ/m3 83
570
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 7.1
24
Strength to Weight: Bending, points 9.3
22
Thermal Diffusivity, mm2/s 110
11
Thermal Shock Resistance, points 8.1
19

Alloy Composition

Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Cadmium (Cd), % 0 to 0.00010
0
Calcium (Ca), % 0
0.00050 to 0.015
Carbon (C), % 0
0.1 to 0.15
Chromium (Cr), % 0
2.7 to 3.3
Copper (Cu), % 99.99 to 99.999
0 to 0.25
Iron (Fe), % 0 to 0.0010
93.8 to 95.8
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0 to 0.00050
0.3 to 0.6
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 0 to 0.0010
0 to 0.25
Niobium (Nb), % 0
0.015 to 0.070
Phosphorus (P), % 0.0010 to 0.0060
0 to 0.020
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0 to 0.1
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.010
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
0
Titanium (Ti), % 0
0 to 0.015
Vanadium (V), % 0
0.2 to 0.3
Zinc (Zn), % 0 to 0.00010
0