CR022A Copper vs. AWS E80C-Ni2

CR022A copper belongs to the copper alloys classification, while AWS E80C-Ni2 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is CR022A copper and the bottom bar is AWS E80C-Ni2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 15
27
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
72
Tensile Strength: Ultimate (UTS), MPa 230
620
Tensile Strength: Yield (Proof), MPa 140
540

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Melting Completion (Liquidus), °C 1090
1450
Melting Onset (Solidus), °C 1040
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 380
52
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 100
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 31
3.3
Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.6
Embodied Energy, MJ/kg 41
22
Embodied Water, L/kg 310
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
160
Resilience: Unit (Modulus of Resilience), kJ/m3 83
770
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 7.1
22
Strength to Weight: Bending, points 9.3
21
Thermal Diffusivity, mm2/s 110
14
Thermal Shock Resistance, points 8.1
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Cadmium (Cd), % 0 to 0.00010
0
Carbon (C), % 0
0 to 0.12
Copper (Cu), % 99.99 to 99.999
0 to 0.35
Iron (Fe), % 0 to 0.0010
93.8 to 98.3
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0 to 0.00050
0 to 1.5
Nickel (Ni), % 0 to 0.0010
1.8 to 2.8
Phosphorus (P), % 0.0010 to 0.0060
0 to 0.025
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0 to 0.9
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.030
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
0
Vanadium (V), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.00010
0
Residuals, % 0
0 to 0.5